Mildew Resistant PVC Truck Cover Tarps PVC Coated Tarpaulin Cover for Plain Style Trucks

Mildew Resistant PVC Truck Cover Tarps PVC Coated Tarpaulin Cover for Plain Style Trucks

Technical Specifications

Product Details

• Composition: PVC +  Polyester Mesh Fabric + PVC 
• Thickness: Medium weight
• Effective Width: 1-3.2M
• Roll Length: 50M / 100M
• Minimum Order Quantity (MOQ): 3000 Meters

Processing & Customization

• Processing Methods: Sewing, Hot-Air Welding, High-Frequency Welding
• Customization Options: Thickness, Weight, Color, Base Fabric, Width, Roll Length, Special Attributes

Product Performance

Q: What standards are used to verify the anti mold performance of the product? What is the actual effect?
A: According to GB/T 24346 testing, the anti mold grade meets the first level standard, with an inhibition rate of ≥ 99% against common molds such as Aspergillus niger, Penicillium, and Aspergillus flavus. After continuous use for 18 months in southern regions with humidity above 90%, there are no visible mold spots on the surface of the tarpaulin, effectively protecting the goods from mold contamination and extending the lifespan of the tarpaulin by more than three times.
Q: Can the basic mechanical properties of "plain color truck tarpaulin" meet long-distance transportation requirements?
A: Using 1000D high-strength polyester base fabric, the tear strength in the warp/weft direction is ≥ 160N/75N (GB/T3917.3), and the tensile strength is ≥ 1980N/1480N/5cm (GB/T3923.1), which can resist frequent scratching and pulling during transportation. After driving a total of 160000 kilometers, the strength retention rate is greater than 90%.
Q: What data supports the weather resistance and waterproof performance of the product?
A: Through the -25 ℃ low-temperature bending crack free test (FZ/T01007), the temperature resistance range is -30 ℃ to+70 ℃. The hydrostatic pressure is ≥ 50kPa (FZ/T01004), and the goods are kept dry after continuous rainstorm. The flame retardant performance has a continuous combustion time of only 0.2 seconds (national standard ≤ 15 seconds), with high-frequency welding reinforcement at the edges and metal reinforcement at the buckle holes, ensuring a service life of over 5 years.